Strong, Extended 10.5"Length Cuff Hand Protection
HandPRO® Fortis500™ Extended Cuff Powder-Free Nitrile Exam Gloves are created from the latest patented LOW DERMA™ technology* accelerator-free nitrile. Black charcoal matte color, this glove is thicker (5.0mil) than your average exam glove and features an ideal-length 10.5"L (260mm L) extended cuff for exceptional hand protection in demanding, high-risk environments.
First Fentanyl permeation labeling claim granted by the U.S. FDA. Fortis500 has passed the most stringent test method with Fentanyl Citrate permeation base on 0.01 microgram/cm²/min (simulating the worst-case scenario) for protection against accidental second-hand exposure that can cause respiratory depression, arrest, and possibly death. It's protection you can trust.
Features and Benefits
- Advanced X-Linking Nitrile - Strength you can trust
- Patented LOW DERMA™ Technology Accelerator-Free Nitrile
- FDA Approved Low Dermatitis Potential
- Not made with dithiocarbamates, thiurams or mercaptobenzothiazoles (MBT)
- Sulfur-Free & Thiuram-Free
- Not Made with Natural Rubber Latex - Reduces risk of latex sensitization
- Chemotherapy Drug Permeation Tested - Safe for use with certain chemotherapy drugs
- Fentanyl Citrate Permeation Tested - No breakthrough > 240 minutes
- Textured Fingertips - Enhanced tactile sensitivity
- Powder-Free - The medical exam glove standard
Specifications
Meet or exceed ASTM and FDA requirements.
Packaging
100 Gloves/Box, 10 Boxes/Case (1000 gloves); XXL size (900 gloves
| Certifications/Compliance | Meets or exceeds ASTM and FDA requirements. NFPA 1999; ASTM 1671; ASTM 6978; ASTM F739; MDR (EU) 2017/745; PPE (EU) 2016/425, Category III. |
| Material | Accelerator-Free Nitrile |
| Color | Charcoal Matte Black |
| Extra Length | 10.5" / 260 mm |
| Cuff Thickness | 0.07 mm / 2.7 mils |
| Palm Thickness | 0.09 - 0.10 mm / 3.5 - 3.9 mils |
| Fingertip Thickness | 0.13 - 0.14 mm / 5.1 - 5.5 mils |
| Hand | Ambidextrous |
| Texture | Fingertip-Textured |
| Powder Free | Yes |
| Latex | Not made with natural rubber latex |
| Tensile Strength | 27 - 33 MPa (after aging) |
| Ultimate Elongation | 600 - 640% (after aging) |
| Force at Break | 7.5 - 8.2 Newton |